NAGALE
NAGALE is a 0.6mm PU leather on a nylon base, built for parts that rest against the skin for hours: headphone ear cushions and headbands, and the face cushions and straps of AR and VR headsets. Wet and dry PU layers give it a soft, premium hand feel and excellent drape, and a softening finish after the dry process makes the surface even smoother to the touch. It passes 10% NaOH hydrolysis testing, and surface patterns and colors are made to your specification.
- Soft, premium hand feel: wet and dry PU on a nylon base
- Excellent drape and wearing comfort for parts in contact with skin
- Hydrolysis resistant: passes 10% NaOH for 24 hours at room temperature
- Light at 220 g/m², with 130% elongation across the width
- Custom RP surface patterns and colors
Built to your specification.
Every parameter below can be configured to your exact requirement. Submit your specification with your sample request and we'll develop to match.
Need something beyond these parameters?
The configuration ranges above reflect our standard development envelope for this product family. If your application requires specifications outside these ranges — different base construction, hybrid materials, or entirely new performance characteristics — our R&D team develops custom formulations from scratch.Describe your requirement →
ASTM-verified performance.
Every product is tested to ASTM international standards before delivery. Results below reflect standard black colorway at 25°C, 56% RH.
| Test | Unit | Method | Result |
|---|---|---|---|
| Thickness | mm | ASTM D1777 | 0.6 to 0.7 |
| Weight | g/m² | ASTM D3770 / D3776 | 220 |
| Tensile: Length | kg/2.54cm | ASTM D1682 / D1117 | 12.7 |
| Tensile: Width | kg/2.54cm | ASTM D1682 / D1117 | 6.1 |
| Elongation: Length | % | ASTM D1682 / D1117 | 60 |
| Elongation: Width | % | ASTM D1682 / D1117 | 130 |
| Tear: Length | kg | ASTM D2262 / D1117 | 1.1 |
| Tear: Width | kg | ASTM D2262 / D1117 | 1.2 |
| Hydrolysis | 10% NaOH, 24 hr, room temp | Pass |
Test conditions: 25°C, 56% RH · Validated by JE.B